|Title:||Assessment of current adhesives in class I cavity: Nondestructive imaging using optical coherence tomography and microtensile bond strength|
Adriano Luis Martins
Universidade Estadual de Campinas
University of Washington, Seattle
Tokyo Medical and Dental University
|Citation:||Dental Materials. Vol.31, No.9 (2015), e190-e200|
|Abstract:||© 2015 Academy of Dental Materials. Abstract Objectives To evaluate the sealing ability and the microtensile bond strength (MTBS) of different adhesive systems bonded to dentin in class I cavities. Methods Round tapered dentin cavities (3-mm diameter, 1.5-mm height) prepared in extracted human molars were restored using composite resin (Clearfil Majesty Posterior) with two-step etch-and-rinse adhesive system (Adper Single Bond 2: ASB2), two-step self-etch adhesive (Clearfil SE Bond: CSEB), all-in-one adhesives (G-Bond Plus: GBP; Tri-S Bond Plus: TSBP), or no adhesive (Control), or bonded using low-shrinkage composite with its proper adhesive (Filtek Silorane, Silorane Adhesive System: FSS). After 24-h water storage or 10,000 cycles of thermal stress, the specimens were immersed into a contrast agent. Two and three-dimensional images were obtained using optical coherence tomography (OCT). The mean percentage of high brightness (HB%) at the interfacial zone in cross-sectional images was calculated as an indicator of contrast agent or gap at the interface. The specimens were then sectioned into beams and the MTBS measured. Results The HB% (ASB2 = TSBP = CSEB < FSS = GBP) and MTBS (CSEB = ASB2, CSEB > TSBP = GBP = FSS, ASB2 > FSS) differed significantly among the adhesives. After aging, HB% increased for GBP and FSS specimens, and the MTBS decreased for FSS specimens (ANOVA, Tukey's post hoc, p < 0.05). The HB% and MTBS were significantly and negatively correlated (p = 0.002). Confocal laser scanning and scanning electron micrographs confirmed contrast agent infiltration within the gap. Significance There was a significant correlation between sealing performance and bond strength of the adhesives in the whole cavity. After aging, the two-step systems showed equal or superior performance to the all-in-one and Silorane systems.|
|Appears in Collections:||Scopus 2011-2015|
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.