Warunee KlinklaiSeiichi KawaharaTomonobu MizumoMasahiro YoshizawaJitladda Tangpakdee SakdapipanichYoshinobu IsonoHiroyuki OhnoNagaoka University of TechnologyTokyo University of Agriculture and TechnologyMahidol University2018-07-242018-07-242003-08-01European Polymer Journal. Vol.39, No.8 (2003), 1707-1712001430572-s2.0-0037810770https://repository.li.mahidol.ac.th/handle/20.500.14594/20812Preparation of liquid epoxidized natural rubber (ENR) was made by oxidative depolymerization of ENR in latex stage without loss of epoxy group. Epoxidation of fresh natural rubber latex, which was purified by deproteinization with proteolytic enzyme and surfactant, was carried out with freshly prepared peracetic acid. The glass transition temperature (Tg) and gel content of the rubbers increased after the epoxidation, both of which were dependent upon an amount of peracetic acid. The gel content was significantly reduced by oxidative depolymerization of the rubber with (NH4)2S2O8in the presence of propanal. The resulting liquid epoxidized rubber (Mn≈ 104) was found to have well-defined terminal groups, i.e. aldehyde groups and α-β unsaturated carbonyl groups. The novel rubber was applied to transport Li+as an ionic conducting medium, that is, solid polymer electrolyte. © 2003 Elsevier Ltd. All rights reserved.Mahidol UniversityChemistryMaterials SciencePhysics and AstronomyArticleSCOPUS10.1016/S0014-3057(03)00060-0