Publication: Conductive nanocomposite aligned fibers of PVA-AgNPs-PEDOT/PSS
Issued Date
2014-01-01
Resource Type
ISSN
16628985
10226680
10226680
Other identifier(s)
2-s2.0-84920828741
Rights
Mahidol University
Rights Holder(s)
SCOPUS
Bibliographic Citation
Advanced Materials Research. Vol.1033-1034, (2014), 1009-1019
Suggested Citation
Prasit Pisesweerayos, Somsak Dangtip, Pitt Supaphol, Toemsak Srikhirin Conductive nanocomposite aligned fibers of PVA-AgNPs-PEDOT/PSS. Advanced Materials Research. Vol.1033-1034, (2014), 1009-1019. doi:10.4028/www.scientific.net/AMR.1033-1034.1009 Retrieved from: https://repository.li.mahidol.ac.th/handle/20.500.14594/33875
Research Projects
Organizational Units
Authors
Journal Issue
Thesis
Title
Conductive nanocomposite aligned fibers of PVA-AgNPs-PEDOT/PSS
Other Contributor(s)
Abstract
© (2014) Trans Tech Publications, Switzerland. Poly(vinyl alcohol)-silver nanoparticles (PVA:AgNPs), and poly(vinyl alcohol)-silver nanoparticles-poly(3, 4-ethylene dioxythiophene)/poly(styrene sulfonate) (PVA:AgNPs: PEDOT/ PSS) were generated as ultra-fine electrospun fibers using the aligned fiber mat and aligned single fiber techniques. SEM and TEM were used to confirm the morphology, diameter size, and fiber alignment of the ultra-fine fibers. A two-probe technique was utilized to assess the electrical conductivity of the ultrafine fibers. The highest conductivity of PVA:AgNPs, (10%w/v:0.75%w/v) with a fiber diameter of 0.152 μm, with voltage applied at 17.5 kV within a 20 min collection period in the electrospinning process, was 43.20 S/cm; whereas the highest conductivity of PVA:AgNPs: PEDOT/PSS, (10%w/v:0.25%w/v:0.084%w/v), with a fiber diameter of 0.158 μm and voltage applied at 17.5 kV within a 45 min collection period in the electrospinning process, was 92.18 S/cm.