Publication: Anisotropic mechanical properties of thermoplastic elastomers in situ reinforced with thermotropic liquid-crystalline polymer fibers revealed by biaxial deformations
Issued Date
2005-01-15
Resource Type
ISSN
08876266
Other identifier(s)
2-s2.0-12344288689
Rights
Mahidol University
Rights Holder(s)
SCOPUS
Bibliographic Citation
Journal of Polymer Science, Part B: Polymer Physics. Vol.43, No.2 (2005), 135-144
Suggested Citation
S. Saikrasun, S. Bualek-Limcharoen, S. Kohjiya, K. Urayama Anisotropic mechanical properties of thermoplastic elastomers in situ reinforced with thermotropic liquid-crystalline polymer fibers revealed by biaxial deformations. Journal of Polymer Science, Part B: Polymer Physics. Vol.43, No.2 (2005), 135-144. doi:10.1002/polb.20315 Retrieved from: https://repository.li.mahidol.ac.th/handle/20.500.14594/16455
Research Projects
Organizational Units
Authors
Journal Issue
Thesis
Title
Anisotropic mechanical properties of thermoplastic elastomers in situ reinforced with thermotropic liquid-crystalline polymer fibers revealed by biaxial deformations
Author(s)
Other Contributor(s)
Abstract
The anisotropic mechanical properties of the thermoplastic elastomer (TPE) in situ reinforced with thermotropic liquid-crystalline polymer (TLCP) fibers were investigated by uniaxial, strip-biaxial, and equibiaxial tensile measurements. The in situ composite sheets were prepared from an immiscible blend of a TLCP, Rodrun LC3000, and a TPE, styrene-(ethylene butylene)-styrene (SEBS) triblock copolymer, by a melt extrusion process. The uniaxial orientation of the TLCP fibers in the TPE matrix generated during processing yielded a significant mechanical anisotropy in the composites. The biaxial tensile measurements clearly demonstrated the anisotropic mechanical properties of the composites: The modulus in the direction parallel to the machine direction (MD) was considerably higher than that in the transverse direction (TD), even at large deformations; in equibiaxial stretching, the yield strain in the MD was smaller than that in the TD; the composite containing 10 wt % of TLCP exhibited the highest mechanical anisotropy among the composites, with 0-30 wt % TLCP. The latter result was in accord with the SEM observation that the composite with 10 wt % of TLCP possessed the best fibrillar morphology and the highest degree of uniaxial orientation of the TLCP fibers. The yield strains in uni- and biaxial elongation for the composite containing 10 wt % of TLCP were almost the same as those for the neat styrene-ethylene butylene-styrene. The TLCP phase with good fibrillation did not appreciably alter the original yielding characteristics of the elastomer matrix. © 2004 Wiley Periodicals, Inc.