Publication: Gas/solid reaction during sintering of Si<inf>3</inf>N<inf>4</inf>ceramics in an air furnace
Issued Date
2007-01-01
Resource Type
ISSN
09552219
Other identifier(s)
2-s2.0-33751565447
Rights
Mahidol University
Rights Holder(s)
SCOPUS
Bibliographic Citation
Journal of the European Ceramic Society. Vol.27, No.4 (2007), 2111-2117
Suggested Citation
Nirut Wangmooklang, Kuljira Sujirote, Supatra Jinawath, Shigetaka Wada Gas/solid reaction during sintering of Si<inf>3</inf>N<inf>4</inf>ceramics in an air furnace. Journal of the European Ceramic Society. Vol.27, No.4 (2007), 2111-2117. doi:10.1016/j.jeurceramsoc.2006.06.004 Retrieved from: https://repository.li.mahidol.ac.th/handle/20.500.14594/24611
Research Projects
Organizational Units
Authors
Journal Issue
Thesis
Title
Gas/solid reaction during sintering of Si<inf>3</inf>N<inf>4</inf>ceramics in an air furnace
Other Contributor(s)
Abstract
Solid/gas reaction during sintering of Si3N4ceramics in an air atmosphere was investigated. The Si3N4specimens were prepared from β-powder with MgO and Al2O35 wt% each as sintering aids. The oxygen content of the mixtures after milling increased with increasing milling time. The SiO2content was found to cause more significant mass loss of the sintered specimens than the sintering temperature. There was also a gradient of the oxygen partial pressure (PO2) in the crucible during sintering resulting in the formation of silicon oxynitride (Si2N2O) on the surfaces of Si3N4specimens in different quantities. The mass loss reaction, amount of mass loss as a function of soaking time and sintering temperature, mass loss difference between the top and the bottom of specimens and the formation of Si2N2O are discussed. © 2006 Elsevier Ltd. All rights reserved.