Publication: Controlled degradation of natural rubber and modification of the obtained telechelic oligoisoprenes: Preliminary study of their potentiality as polyurethane foam precursors
Issued Date
2010-08-01
Resource Type
ISSN
10974628
00218995
00218995
Other identifier(s)
2-s2.0-77952057711
Rights
Mahidol University
Rights Holder(s)
SCOPUS
Bibliographic Citation
Journal of Applied Polymer Science. Vol.117, No.3 (2010), 1279-1289
Suggested Citation
Anuwat Saetung, Adisai Rungvichaniwat, Irène Campistron, Pairote Klinpituksa, Albert Laguerre, Pranee Phinyocheep, Jean François Pilard Controlled degradation of natural rubber and modification of the obtained telechelic oligoisoprenes: Preliminary study of their potentiality as polyurethane foam precursors. Journal of Applied Polymer Science. Vol.117, No.3 (2010), 1279-1289. doi:10.1002/app.31907 Retrieved from: https://repository.li.mahidol.ac.th/handle/20.500.14594/28931
Research Projects
Organizational Units
Authors
Journal Issue
Thesis
Title
Controlled degradation of natural rubber and modification of the obtained telechelic oligoisoprenes: Preliminary study of their potentiality as polyurethane foam precursors
Other Contributor(s)
Abstract
Telechelic oligoisoprenes were successfully prepared by the selective controlled degradation of natural rubber, a renewable source, via epoxidation and cleavage reactions. The molar mass of the oligoisoprene product obtained depends on the degree of epoxidation of the starting materials. The chemically modified structures obtained via epoxidation, hydrogenation, and ring opening of epoxide groups were also studied, and the chemical structures and thermal properties of the oligoisoprene products were determined. Moreover, the preliminary study of preparation of hydroxytelechelic natural rubber (HTNR)-based polyurethane foam was performed. A novel HTNR-based polyurethane foam was successfully prepared and its thermal properties were investigated and the results indicated that the HTNR-based polyurethane foam has a good low temperature flexibility. © 2010 Wiley Periodicals, Inc.