Publication: Development of dental implant coating with minocycline-loaded niosome for antibacterial application
Issued Date
2020-04-01
Resource Type
ISSN
17732247
Other identifier(s)
2-s2.0-85079521491
Rights
Mahidol University
Rights Holder(s)
SCOPUS
Bibliographic Citation
Journal of Drug Delivery Science and Technology. Vol.56, (2020)
Suggested Citation
Nattarat Wongsuwan, Anupma Dwivedi, Salunya Tancharoen, Norased Nasongkla Development of dental implant coating with minocycline-loaded niosome for antibacterial application. Journal of Drug Delivery Science and Technology. Vol.56, (2020). doi:10.1016/j.jddst.2020.101555 Retrieved from: https://repository.li.mahidol.ac.th/handle/20.500.14594/53900
Research Projects
Organizational Units
Authors
Journal Issue
Thesis
Title
Development of dental implant coating with minocycline-loaded niosome for antibacterial application
Other Contributor(s)
Abstract
© 2020 Elsevier B.V. Peri-implant diseases are mostly caused by a bacterial infection which leads to inflammation and bone loss at and around the implant. In this study, minocycline-loaded niosomes prepared by thin-film hydration method were coated on the dental implant for antibacterial application. Minocycline-loaded-niosomes were characterized for drug loading content, encapsulation efficiency and yield. Result demonstrated that the optimum formulation was 3:1 comprising of span 60 and cholesterol which provided the most drug loading content and encapsulation efficiency. The optimum coating cycles were 120 which could coat the highest content of drug on coated dental implants. In vitro drug release from the coated implants was studied. Antibacterial activity and cytotoxicity of the coated implant were also investigated. Results suggested that minocycline-release from the coated dental implant could be controlled for up to 7 days which was a crucial period after implantation. During this time, inhibition of Porphylomonas gingivalis was also noticed. In vitro cytotoxicity study revealed that the coated implant was non-toxic to osteoblast cells. Hence, results suggest that this coating strategy can be used for antibacterial coating of medical devices.