Publication: The effect of silane carriers on silane grafting of high-density polyethylene and properties of crosslinked products
Issued Date
2010-12-01
Resource Type
ISSN
01429418
Other identifier(s)
2-s2.0-77956401448
Rights
Mahidol University
Rights Holder(s)
SCOPUS
Bibliographic Citation
Polymer Testing. Vol.29, No.8 (2010), 958-965
Suggested Citation
Kalyanee Sirisinha, Marnviga Boonkongkaew, Soontaree Kositchaiyong The effect of silane carriers on silane grafting of high-density polyethylene and properties of crosslinked products. Polymer Testing. Vol.29, No.8 (2010), 958-965. doi:10.1016/j.polymertesting.2010.08.004 Retrieved from: https://repository.li.mahidol.ac.th/handle/20.500.14594/28910
Research Projects
Organizational Units
Authors
Journal Issue
Thesis
Title
The effect of silane carriers on silane grafting of high-density polyethylene and properties of crosslinked products
Other Contributor(s)
Abstract
High-density polyethylene (HDPE) was melt-grafted with vinyl trimethoxysilane using dicumyl peroxide as initiator. Three types of ethylene copolymers were used as silane carriers, and were evaluated for their ability to assist the silane-grafting and water-crosslinking of HDPE. FTIR revealed that an increase in the amount of silane absorbed in the carriers did not help improve the silane-grafting efficiency. However, the gel and rheological results showed that those carriers promoted the rate of crosslinking and increased the density of the crosslink network. Ethylene vinyl acetate showed a stronger effect in this respect than ethylene octene and ethylene-butene copolymers. Analysis of the crosslinked materials by heat distortion temperature (HDT) test and thermogravimetric analysis (TGA) indicated a marked increase in distortion and decomposition temperatures, as well as thermal activation energy, compared to the neat HDPE. The presence of silane crosslink also resulted in a slight improvement in tensile yield stress and modulus. © 2010 Elsevier Ltd. All rights reserved.