Development of metal-resin composite restorative material. Part 3. Flexural properties and condensability of metal-resin composite using Ag-Sn irregular particles.

dc.contributor.authorS. Urapeponen_US
dc.contributor.authorK. Kakutaen_US
dc.contributor.authorH. Oguraen_US
dc.contributor.authorC. Suchatlampongen_US
dc.contributor.authorA. Rittapaien_US
dc.contributor.otherMahidol Universityen_US
dc.date.accessioned2018-09-07T09:10:31Z
dc.date.available2018-09-07T09:10:31Z
dc.date.issued2000-01-01en_US
dc.description.abstractPowder-liquid type metal-resin composites, using Ag-Sn irregular particles as the filler, 4-META as coupling agent and UDMA + TEGDMA as resin matrix, were experimentally prepared under 9 different conditions (three different particle sizes and three different filler contents). The flexural strength and flexural modulus were measured. Three different irregular particle size MRCs without redox-initiator at 94% filler content, as well as amalgam, conventional hybrid composite and Ag-Sn spherical particle MRC were evaluated for condensability. The flexural strength of the Ag-Sn irregular particle MRC was significantly influenced by both the filler particle size and filler contents (p < 0.01). It increased when either the filler content increased or the particles size decreased. The highest flexural strength (97.6 MPa) was obtained from the condition of particles size < 20 microns and 94% filler content. The flexural modulus was significantly influenced by filler content and it increased with increasing filler content. The condensability of the Ag-Sn irregular particle MRC was lower than that of amalgam but much higher than presently available conventional composites and spherical particle MRC.en_US
dc.identifier.citationDental materials journal. Vol.19, No.2 (2000), 186-195en_US
dc.identifier.doi10.4012/dmj.19.186en_US
dc.identifier.issn02874547en_US
dc.identifier.other2-s2.0-0034208195en_US
dc.identifier.urihttps://repository.li.mahidol.ac.th/handle/20.500.14594/25927
dc.rightsMahidol Universityen_US
dc.rights.holderSCOPUSen_US
dc.source.urihttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=0034208195&origin=inwarden_US
dc.subjectDentistryen_US
dc.subjectMaterials Scienceen_US
dc.titleDevelopment of metal-resin composite restorative material. Part 3. Flexural properties and condensability of metal-resin composite using Ag-Sn irregular particles.en_US
dc.typeArticleen_US
dspace.entity.typePublication
mu.datasource.scopushttps://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=0034208195&origin=inwarden_US
Files
Collections