Enhancing elemental release and antibacterial properties of resin-based dental sealants with calcium phosphate, bioactive glass, and polylysine
Issued Date
2025-01-18
Resource Type
eISSN
14726831
Scopus ID
2-s2.0-85216439769
Pubmed ID
39827118
Journal Title
BMC oral health
Volume
25
Issue
1
Rights Holder(s)
SCOPUS
Bibliographic Citation
BMC oral health Vol.25 No.1 (2025) , 96
Suggested Citation
Lertwisitphon P., Worapasphaiboon Y., Champakanan N., Toneluck A., Naruphontjirakul P., Young A.M., Chinli R., Chairatana P., Sucharit S., Panpisut P. Enhancing elemental release and antibacterial properties of resin-based dental sealants with calcium phosphate, bioactive glass, and polylysine. BMC oral health Vol.25 No.1 (2025) , 96. doi:10.1186/s12903-025-05489-2 Retrieved from: https://repository.li.mahidol.ac.th/handle/20.500.14594/104203
Title
Enhancing elemental release and antibacterial properties of resin-based dental sealants with calcium phosphate, bioactive glass, and polylysine
Corresponding Author(s)
Other Contributor(s)
Abstract
BACKGROUND: This study aimed to develop ion-releasing and antibacterial resin-based dental sealants comprising 3 to 6 wt% monocalcium phosphate monohydrate (MCPM, M), 3 to 6 wt% bioactive glass (BAG, B), and 3 to 6 wt% polylysine (PLS, P). The physical properties, mechanical performance, cytotoxicity, and inhibition of S. mutans biofilm by these materials were subsequently evaluated. METHODS: Five experimental dental sealants were formulated as follows: F1 (M6B6P6), F2 (M6B6P3), F3 (M3B3P6), F4 (M3B3P3), and F5 (M0B0P0, serving as the control). ClinproXT (CP, 3 M, Saint Paul, MN, USA) was used for commercial comparison. The degree of monomer conversion (DC) was determined using attenuated total reflectance-Fourier transform infrared spectroscopy (n = 5). The biaxial flexural strength (n = 6) and Vickers surface microhardness (n = 5) of the materials were evaluated after a 24-hour immersion in water. The element release over 4 weeks was measured using inductively coupled plasma-optical emission spectrometry (ICP-OES) (n = 3). The cell viability of mouse fibrosarcoma cells exposed to the extract was assessed via an MTT assay (n = 3). Additionally, the inhibition of S. mutans biofilm was tested (n = 3). Statistical analysis was conducted using one-way ANOVA and the Tukey HSD test. RESULTS: The lowest DC among experimental sealants was obtained from F1 (66 ± 4%), which was significantly higher than CP (54 ± 2%, p < 0.001). The lowest biaxial flexural strength was obtained from F3 (131 ± 47 MPa). This was comparable to that of CP (140 ± 58 MPa, p = 0.992). The lowest surface microhardness among experimental materials was detected with F2 (19 ± 2 Vickers hardness number), which was higher than that of CP (12 ± 1 Vickers hardness number, p = 0.003). Furthermore, high cell viability of > 90% after exposure to extracts from the experimental materials was detected, which was similar to that observed with CP. Additionally, the experimental materials exhibited higher Ca and P release compared to CP and showed a potential trend for reducing S. mutans biofilm formation. Increasing additive concentrations exhibited minimal effects on material properties, except for enhanced elemental release and a slight reduction in BFM with higher PLS content. CONCLUSION: The experimental sealants provided sufficient physical and mechanical strength and maintained cell viability and bacterial inhibition with higher elemental release than the commercial product.