A study of effect of welding parameter to ferrite content of 2205 duplex stainless steel by Gas Tungsten Arc Welding process (GTAW)

Abstract

The development of an adequate welding procedure for a duplex stainless steel grade 2205 is the main target of this research. The effects of welding parameters using welding by ER2209 filler metal are investigated practically in an industrial qualification program. Gas Tungsten Arc Welding (GTAW) is a fabrication field process on a material-pipe form. The main target of the qualified welding procedure is to achieve a ferrite content range of 35-65% on the welded metal (WM) and heat affected zone (HAZ). Welding speed ranges and welding sequence direction were varied in order to observe the ferrite contents. It was concluded that by control of the welding speed at high speed under sound weld results, the ferrite content is acceptable within a 35-65% ferrite content range. However, when welding at lower speeds under sound weld results, the ferrite content is unacceptable within that 35-65% ferrite content range. The research outcome could be applied to a qualified-procedure package in a chemical plant or off-shore site.

การพัฒนาขั้นตอนการเชื่อมที่เหมาะสมสำหรับเหล็กกล้าไร้สนิมดูเพล๊กซ์ เกรด 2205 คือวัตถุประสงค์หลักของโครงการวิจัยนี้ ผลกระทบของพารามิเตอร์การเชื่อมที่เชื่อมด้วยลวดเชื่อมเกรด ER2209มีการพิจารณาจากการใช้งานในอุตสาหกรรมที่ปฏิบัติจริง การเชื่อมอาร์คทังสเตน (GTAW) เป็นกระบวนการผลิตในรูปแบบวัสดุที่เป็นท่อเป้าหมายหลักของขั้นตอนการเชื่อมคือการได้รับค่าปริมาณเฟอร์ไรท์ในช่วง 35-65% บนรอยเชื่อมและบริเวณกระทบร้อน ช่วงความเร็วของการเชื่อมและการจัดลำดับทิศทางการเชื่อมมีผลต่อการแปรเปลี่ยนของค่าปริมาณเฟอร์ไรท์ สรุปได้ว่าการควบคุมความเร็วการเชื่อมที่ความเร็วสูง ได้ผลสรุปคือค่าปริมาณเฟอร์ไรท์ยอมรับได้ในช่วง 35-65% แต่การควบคุมความเร็วการเชื่อมที่ความเร็วที่ต่ำ ค่าปริมาณเฟอร์ไรท์ยอมรับไม่ได้ในช่วง 35-65% ของค่าปริมาณเฟอร์ไรท์ ผลการวิจัยสามารถนำขั้นตอนการเชื่อมไปใช้งานในอุตสาหกรรมปิโตรเคมีหรือแท่นผลิตนอกชายฝั่งได้