Development of Green Leather Alternative from Natural Rubber and Pineapple Leaf Fiber
Issued Date
2023-11-01
Resource Type
eISSN
20711050
Scopus ID
2-s2.0-85193552895
Journal Title
Sustainability (Switzerland)
Volume
15
Issue
21
Rights Holder(s)
SCOPUS
Bibliographic Citation
Sustainability (Switzerland) Vol.15 No.21 (2023)
Suggested Citation
Duangsuwan S., Junkong P., Phinyocheep P., Thanawan S., Amornsakchai T. Development of Green Leather Alternative from Natural Rubber and Pineapple Leaf Fiber. Sustainability (Switzerland) Vol.15 No.21 (2023). doi:10.3390/su152115400 Retrieved from: https://repository.li.mahidol.ac.th/handle/20.500.14594/98480
Title
Development of Green Leather Alternative from Natural Rubber and Pineapple Leaf Fiber
Author's Affiliation
Corresponding Author(s)
Other Contributor(s)
Abstract
In the present research, a plant-based leather substitute material or leather alternative was developed from natural rubber (NR) and pineapple leaf fiber (PALF) using a simple process. Pineapple leaf fiber was extracted from waste pineapple leaves using a mechanical method. Untreated PALF (UPALF) and sodium hydroxide-treated PALF (TPALF) were then formed into non-woven sheets using a paper making process. PALF non-woven sheets were then coated with compounded natural rubber latex at three different NR/PALF ratios, i.e., 60/40, 50/50, and 40/60. Epoxidized natural rubber with an epoxidation level of 10% (ENR) was used as an adhesion promoter, and its content was varied at 5, 10, and 15% by weight of the total rubber. The obtained leathers were characterized in terms of tensile properties, tear strength, and hardness. The internal structure of the leathers was observed with a scanning electron microscope. Comparison of these properties was made against those reported in the literature. It was found that the leather with NR/PALF equal to 50/50 was the most satisfactory; that prepared from TPALF was softer and had greater extension at break. With the addition of ENR at 5%, the stress-strain curve of each respective leather increased significantly, and as the amount of ENR was increased to 10 and 15%, the stresses at corresponding strains dropped to lower values but remained higher than that without ENR. PALF leather prepared in this study has comparable or better properties than other alternative leathers reported in the literature and is much stronger than that made from mushrooms. Thus, this type of leather alternative offers unique characteristics of being bio-based and having a lower carbon footprint.