Study of the preparation of NR/NBR laminates

Abstract

The present work involved studies to improve the peel strength of NR/NBR laminates. The effect compounding ingredients such as liquid polymer, epoxidised natural rubber and epoxidised liquid natural rubber were determined. The effect of contact time, contact temperature and rubber viscosity were investigated. The effect of commercial adhesive and chlorination on NR/NBR adhesion were also studied. The result obtained show that compounding by addition of liquid polymer, epoxidised natural rubber and tackifier could improve the peel strength by 7-9 times. The contact time for optimum peel strength was found to be the appropriate was 10 minutes and contact temperature should be at 100 C. The lowering of NBR compound viscosity to match that of NR compound resulted in increasing peel strength by 3.4 times. The commercial adhesive were found to give highest peel strength by 32 times. Chlorination of NR compound could improve the peel strength 3 times higher than that of the untreated specimen.

งานวิจัยนี้เป็นการศึกษาปรับปรุงคุณสมบัติ การติดกันระหว่างยางธรรมชาติและยางไนไตรล์ ศึกษาผลของ โพลิเมอร์เหลว ยางธรรมชาติชนิดอีพอกซิไดซ์ สารช่วย การติด (Tackifier) เวลาและอุณหภูมิที่ใช้ในการติด ความหนืดของยาง การทำ Chlorination บนผิวยางธรรมชาติ และการใช้กาวยูรีเทน และนีโอพรีน ผลการศึกษาพบว่า การผสมโพลิเมอร์เหลว ยางธรรมชาติ ชนิดอีพอกซิไดซ์ สารช่วยการติด (Tackifier) สามารถเพิ่ม ค่า Peel Strength ได้ 7-9 เท่าเวลาที่ใช้ในการติดกันของ ยางที่ 10 นาที อุณหภูมิที่ใช้ติด 100 องศาเซลเซียส ให้ค่า Peel Strength สูงสุด การลดความหนืดของยางไนไตรล์ให้ เท่ากับยางธรรมชาติ สามารถเพิ่มค่า Peel strength ได้ 3.4 เท่า การใช้กาวยูรีเทนและยางนีโอพรีน สามารถถเพิ่ม ค่า Peel Strength ได้สูงที่สุดถึง 32 เท่า การทำ Chlorination บนผิวยางธรรมชาติ สามารถเพิ่มค่า Peel Strength ได้ 3 เท่า