6 results
Search Results
Now showing 1 - 6 of 6
Publication Metadata only Properties of experimental copper-aluminiumnickel alloys for dental post-and-core applications(2014-01-01) Apiwat Rittapai; Somchai Urapepon; Julathep Kajornchaiyakul; Choltacha Harniratisai; Mahidol University; National Metal and Materials Technology Center (MTEC)PURPOSE: This study aimed to develop a copper-aluminium-nickel alloy which has properties comparable to that of dental alloys used for dental post and core applications with the reasonable cost. MATERIALS AND METHODS: Sixteen groups of experimental... copper alloys with variants of 3, 6, 9, 12 wt% Al and 0, 2, 4, 6 wt% Ni were prepared and casted. Their properties were tested and evaluated. The data of thermal, physical, and mechanical properties were analyzed using the two-way ANOVA and Tukey's testPublication Metadata only Development of Metal-resin Composite Restorative Material Part 4 Flexural Strength and Flexural Modulus of Metal-resin Composite using Ag-In Alloy Particles as Filler(2002-01-01) Kiyoshi Kakuta; Somchai Urapepon; Yukio Miyagawa; Hideo Ogura; Masahiko Yamanaka; Chatcharee Suchatlampong; Apiwat Rittapai; Nippon Dental University; Mahidol UniversityThe flexural strength and flexural modulus of an experimental metal-resin composite, which used Ag-In alloy particle as the filler, were evaluated. The effect of acid treatment and heat treatment on the Ag-In alloy particle was investigated... of HCl of the acid treatment. A metal-resin composite, which used acid-treated and 350°C heat-treated Ag-In alloy fillers, matched the requirement of strength of ISO 4049. The average of flexural modulus of the experimental metal-resin composite was 9Item Metadata only Development of Cu-Al-Ni alloy for dental post and core application(Mahidol University. Mahidol University Library and Knowledge Center, 2023) Apiwat Rittapai; Somchai Urapepol; Widchaya Kanchanavasita; Kallaya SuputtamongkolGenerally, the technique used for replacement of the tooth is "posts and cores". Noble and semi-precious dental alloys have numerous excellent properties, but they are expensive and unaffordable for lots of patients. The copper-aluminum-nickel alloy... is a reasonably priced alternative, and theoretically is perceived as corrosion resistant. Therefore, this situation could potentially be a prototype to develop a base-metal alloy for dental post and core application, and generate dentistry that is morePublication Metadata only Development of Metal-Resin Composite Restorative Material Part 1 Experimental Composite using Silver-Tin Alloy as Filler and 4-META as Coupling Agent(1999-01-01) Kiyoshi Kakuta; Somchai Urapepon; Yukio Miyagawa; Hideo Ogura; Chatcharee Suchatlampong; Apiwat Rittapai; Nippon Dental University; Mahidol UniversityMetal-resin composites, using metal particles instead of inorganic particles as the filler and 4- META as the coupling agent, were experimentally prepared under 20 different conditions (five different concentrations of 4-META, and four different contents of metal particles). The flexural strength of the prepared metal-resin composites was in the range of about 14.5-61.3 MPa. The flexural strength was significantly influenced by the 4-META concentration, the metal particle content and their interaction. The highest strength was estimated at 2-3 mass% of 4-META concentration and 92.0-93.5 mass% metal filler content. The flexural modulus of the metal resin composite ranged approximately from 7.8 GPa to 15.5 GPa. The flexural modulus of the metal resin composite significantly increased with the metal particle content. The effect of the 4- META concentration on the flexural modulus was not significant.Publication Metadata only Development of Metal-Resin Composite Restorative Material Part 2 Effects of acid and heat treatments of silver-tin filler particles on flexural properties of metal-resin composite(1999-01-01) Somchai Urapepon; Kiyoshi Kakuta; Yukio Miyagawa; Hideo Ogura; Chatcharee Suchatlampong; Apiwat Rittapai; Nippon Dental University; Mahidol Universityfiller particles treated under different conditions were experimentally prepared. The conditions of the alloy particles were; 1) as atomized (NT), 2) 1.8% HCl acid-treated (AT), 3) heat-treated at 150°C for 5 min after AT (A15), 4) heat- treated at 200°CPublication Open Access ความขรุขระผิวของอะมัลกัมที่ผลิตในประเทศไทยภายหลังการขัดและการแปรง(2013-09) พรเกียรติ ชื่นจิตอภิรมย์; Pornkiat Churnjitapirom; ชญาดา เทียนไชย; Chayada Teanchai; อภิวัฒน์ ฤทธาภัย; Apiwat Rittapai; ชญาดา เทียนไชย; Chayada Teanchai; มหาวิทยาลัยมหิดล. คณะทันแพทยศาสตร์. สำนักงานการวิจัยวัตถุประสงค์: เพื่อศึกษาความขรุขระผิวของอะมัลกัมที่ผลิตในประเทศไทยภายหลังจาก การขัดและการแปรงเปรียบเทียบกับอะมัลกัมที่จำหน่ายในท้องตลาด 4 ชนิด คือ Tytin FC, Amalcap Plus, GS-80 spherical และ GS-80 วัสดุอุปกรณ์และวิธีการศึกษา: เตรียมชิ้นตัวอย่างอะมัลกัมในแม่แบบอะคริลิกชนิด ละ 20 ตัวอย่าง เก็บไว้ที่อุณหภูมิ 37 องศาเซลเซียส เป็นเวลา 24 ชั่วโมง จากนั้นนำชิ้น ตัวอย่างทั้งหมดมาขัดด้วยหัวขัดเรียงตามลำดับความหยาบไปจนถึงละเอียดคือ หัวขัด สโตนขาว หัวยางแดงขัดอะมัลกัม และหัวยางเขียวขัดอะมัลกัม นำตัวอย่างอะมัลกัมที่ขัด เสร็จชนิดละ 10 ตัวอย่าง ไปทดสอบความขรุขระผิว เหลือตัวอย่างขัดเสร็จอีกชนิดละ 10 ตัวอย่าง นำไปแปรงกับแปรงสีฟันและสารละลายยาสีฟันด้วยเครื่องแปรงฟัน จากนั้นนำ ไปทดสอบความขรุขระผิว นำค่าความขรุขระผิวมาวิเคราะห์ทางสถิติโดยใช้การวิเคราะห์ ความแปรปรวนทางเดียว และ Tukey’s test เปรียบเทียบพหุคูณที่ระดับนัยสำคัญ 0.05 ผลการศึกษา: ผลการศึกษาพบว่าภายหลังการขัดและการแปรง Tytin FC มีค่าความ ขรุขระผิวน้อยกว่าทุกชนิดอย่างมีนัยสำคัญที่ระดับ 0.05 และในทำนองเดียวกัน GS-80 มีค่าความขรุขระผิวมากกว่าทุกชนิดอย่างมีนัยสำคัญที่ระดับ 0.05 ขณะที่อะมัลกัมไทย, Amalcap Plus และ GS-80 spherical มีค่าความขรุขระผิวไม่ต่างกัน สำหรับการเปรียบ เทียบความขรุขระผิวระหว่างภายหลังการขัดกับการแปรงพบว่าอะมัลกัมทุกผลิตภัณฑ์ ยกเว้น GS-80 ผิวภายหลังการแปรงกับสารละลายยาสีฟันมีค่าความขรุขระมากกว่าการ ขัดอย่างมีนัยสำคัญที่ระดับ 0.05 และ GS-80 มีความขรุขระมากกว่าทุกผลิตภัณฑ์ใน ระดับเดิม บทสรุป: จากผลการตรวจสอบความขรุขระผิวของอะมัลกัมไทยกับอะมัลกัมที่จำหน่ายใน ท้องตลาด 4 ชนิด ภายหลังการขัดและการแปรงพบว่าอะมัลกัมไทยมีความขรุขระผิวใกล้ เคียงหรือน้อยกว่าอะมัลกัมที่จำหน่ายในท้องตลาดบางชนิด คาดว่าอะมัลกัมไทยสามารถ นำไปใช้ทางคลินิกได้อย่างมีประสิทธิภาพ