Publication: Epoxidation of vulcanized natural rubber for bonding to chloroprene rubber
1
Issued Date
2012-03-01
Resource Type
ISSN
15685616
01694243
01694243
Other identifier(s)
2-s2.0-84864699704
Rights
Mahidol University
Rights Holder(s)
SCOPUS
Bibliographic Citation
Journal of Adhesion Science and Technology. Vol.26, No.6 (2012), 783-792
Suggested Citation
Siriwat Radabutra, Taweechai Amornsakchai, Sombat Thanawan Epoxidation of vulcanized natural rubber for bonding to chloroprene rubber. Journal of Adhesion Science and Technology. Vol.26, No.6 (2012), 783-792. doi:10.1163/016942411X580009 Retrieved from: https://repository.li.mahidol.ac.th/handle/123456789/13984
Research Projects
Organizational Units
Authors
Journal Issue
Thesis
Title
Epoxidation of vulcanized natural rubber for bonding to chloroprene rubber
Other Contributor(s)
Abstract
Vulcanized natural rubber (NR) sheet was epoxidized in performic acid solution (6 moles of 30% H 2 O 2 + 2 moles of formic acid) for 0-120 min under ambient conditions. Degree of epoxidation determined by ATR-IR increased with epoxidation time up to 60 min while at 120 min most of the epoxide rings of epoxidized NR (ENR) were opened up. Atomic Force Microscopy (AFM) was used to characterize surface properties of ENR. It indicated that both relative stiffness and roughness increased gradually as compared to control NR. Peel strength between ENR and chloroprene rubber (CR) increased up to 30 min of epoxidation time and then decreased. It was concluded that optimum peel strength was attributed to the balance between chemical interaction (epoxide groups on ENR with allyl chlorine groups on CR) and physical properties of ENR surface. Koninklijke Brill NV, Leiden, 2012 © 2012 Copyright Taylor and Francis Group, LLC.