Publication: Roles of silane coupling agents on properties of silica-filled polychloroprene
Issued Date
2006-03-01
Resource Type
ISSN
00143057
Other identifier(s)
2-s2.0-30844434286
Rights
Mahidol University
Rights Holder(s)
SCOPUS
Bibliographic Citation
European Polymer Journal. Vol.42, No.3 (2006), 479-486
Suggested Citation
Pongdhorn Sae-Oui, Chakrit Sirisinha, Uthai Thepsuwan, Kannika Hatthapanit Roles of silane coupling agents on properties of silica-filled polychloroprene. European Polymer Journal. Vol.42, No.3 (2006), 479-486. doi:10.1016/j.eurpolymj.2005.09.003 Retrieved from: https://repository.li.mahidol.ac.th/handle/123456789/23178
Research Projects
Organizational Units
Authors
Journal Issue
Thesis
Title
Roles of silane coupling agents on properties of silica-filled polychloroprene
Other Contributor(s)
Abstract
Silane coupling agent is used extensively to improve reinforcing efficiency of silica. Recently, many types of silane coupling agents have been developed and their roles on reinforcing improvement have been studied in many types of rubbers. In the present study, roles of the two widely used silane coupling agents, i.e., bis-(3-triethoxysilylpropyl) tetrasulfane (Si-69) and 3-thiocyanatopropyl triethoxy silane (Si-264) were studied in silica-filled polychloroprene (CR). The results reveal that the presence of Si-69 and Si-264 improves significantly the processability of the rubber compounds. The improvement is more pronounced for Si-264 due to its lower molecular weight and, thus, viscosity. Surprisingly, the results show that Si-69 and Si-264 affect cure characteristics differently, i.e., Si-69 somewhat retards cure while Si-264 accelerates cure. However, both Si-69 and Si-264 result in an increased crosslink density of the vulcanizates. The presence of silane coupling agent also enhances the mechanical properties of the vulcanizates due to the combined effects of better filler dispersion, better rubber-filler interaction and increased crosslink density. A thorough look at the results also reveals that the property enhancement is obvious only at low silane loading (approximately 1.5 phr). Further increase of silane loading generally has little influence on properties of the vulcanizates. In the case of Si-264, excessive use of silane could impair certain properties such as modulus and hardness due to the plasticizing effect. Compared with Si-264, Si-69 imparts the rubber vulcanizates with poorer aging resistance. Explanation goes to the sulfur contribution effect of Si-69. © 2005 Elsevier Ltd. All rights reserved.